Amajor sustainability concern of manufacturing industries is indiscriminate use of lubrication, energy consumption, and allied cost. To avoid such kind of situation and to improve the product quality, sustainable manufacturing concept has been widely used. One of the popular technique is the use of Minimum Quantity Lubrication (MQL) as a working fluid to improve the product performance. Diamond burnishing underMQLenvironment is an exceptional technique to obtain the improved surface integrity of the material without affecting operator health and environmental aspects. In this work, the impact of control factors on the surface integrity characteristics namely surface roughness, surface topography, surface hardness, surface morphology, residual stress and subsurface hardness of 17-4PHstainless steel have been studied underMQLenvironment by using a novel modified tool. It was ensured that minimum surface roughness of 0.05 μmand maximum surface hardness of 405HV had been achieved. Improved surface finish and surface hardness were obtained for a diamond sphere radius of 4mmand 3mmrespectively under optimal diamond burnishing conditions. The obtained investigational results confirm that a novel modified tool was successfully implemented to enhance the surface integrity characteristics under theMQLenvironment. © 2019 IOP Publishing Ltd.

D. Chakradhar

Department of Mechanical Engineering

B. Sachin

S. Narendranath

Fulltext

Indian Institute of Technology Palakkad&nbsp;(IIT Palakkad or IIT PKD) is a public autonomous&nbsp;engineering&nbsp;and&nbsp;research&nbsp;institute located in&nbsp;Palakkad,&nbsp;Kerala. It was&nbsp;one of the five new&nbsp;IITs&nbsp;proposed in the&nbsp;2014 Union budget of India. The campus was inaugurated on 3 August 2015. The institute has 94 faculty, 978 students, and 63 non-teaching staffs.

IT Palakkad currently offers four-year Bachelor of Technology (B.Tech) and two years MS programmes in 8 different engineering disciplines including&nbsp;Computer Science, Electrical, Mechanical, Civil among others.

&nbsp;

IIT Palakkad

Materials Research Express

Diamond burnishing is one of the most popular surface finishing technique used to achieve an excellent surface finish. The aim of the present study is to investigate the effect of process parameters in diamond burnishing of 17-4 PH stainless steel (PH SS) under cryogenic environment. The requirement of a sustainable environment for various machining processes urged to explore the importance of cryogenic burnishing over other cooling techniques. Surface modification was achieved by the application of liquid nitrogen (LN2) during diamond burnishing. The process parameters considered to reduce the surface roughness (Ra) and increase the surface hardness (H) are burnishing speed, burnishing feed and burnishing force. The diamond burnishing experiments were conducted based on the L9 orthogonal array. The significant parameters and the optimal level of each parameters were determined by using analysis of variance (ANOVA) and main effect plots respectively. Multi-response optimization has been carried out for cryogenic diamond burnishing of 17-4 PH stainless steel by using Taguchi's grey relation analysis (TGRA). From the TGRA, it was observed that at burnishing speed 73 m min-1, burnishing feed 0.048 mm/rev and burnishing force 150 N, improved diamond burnishing performance characteristics were obtained. An improvement in grey relation grade (GRG) was found to be 38.47%. Cryogenic diamond burnishing has led to modifications in the microstructure and also an improvement in the subsurface hardness of the material. © 2018 IOP Publishing Ltd.

Experimental evaluation of diamond burnishing for sustainable manufacturing

Diamond burnishing is a cold working process, which produces a work hardened and uniform surface by plastic deformation. The aim of the present work is to study the behavior of diamond burnishing on surface integrity of 17-4 precipitation hardenable stainless steel (PH-SS) under cryogenic, minimum quantity lubrication (MQL) and dry environments. Surface modification was achieved by the application of liquid nitrogen during diamond burnishing. The process parameters considered were speed, feed, burnishing depth and number of passes. Surface integrity characteristics such as microhardness and residual stresses were investigated after diamond burnishing under cryogenic, MQL and dry environments. In cryogenic diamond burnishing, the surface integrity characteristics of 17-4 PH stainless steel has been significantly improved when compared to MQL and dry environments. Maximum microhardness of 395 HV, 369 HV, and 357 HV respectively was observed under cryogenic, MQL and dry environment. The maximum residual stress of -352 MPa, -282 MPa and -195 MPa respectively were recorded for cryogenic, MQL and dry environment. © 2018 Elsevier Ltd. All rights reserved.

Materials Today: Proceedings

Effect of cryogenic diamond burnishing on residual stress and microhardness of 17-4 PH stainless steel

Journal of Manufacturing Processes

Development of novel cutting tool with a micro-hole pattern on PCD insert in machining of titanium alloy

Burnishing avoids the need for super finishing operations after the conventional turning process, to enhance the surface quality. This paper deals with the surface modifications of Al(B4C)p Metal Matrix Composites (MMC) workpiece material after burnishing with a TiAlN coated WC roller. The burnishing speed, lubrication type, burnishing passes, and coating were the input parameters. Surface hardness and roughness after the burnishing were studied. It was found that the coating on the WC roller had enhanced the hardness in the workpiece after burnishing in the case of Al-5 wt.% (B4C)p, under all conditions. The effect of the coating on the work piece surface hardness was not significant with Al-10 wt.% (B4C)p. While burnishing Al-5 wt.% (B4C)p, the minimum surface roughness combined with maximum surface hardness was obtained, during the third pass under dry condition using uncoated rollers. The number of passes to achieve the desired surface conditions reduced, on using coated rollers with kerosene as the lubricant. © 2018 Taylor &amp; Francis.

Journal	Materials Research Express
Publisher	Institute of Physics Publishing
ISSN	20531591